| 填料/增強材料 | | | 特性 | - High Dimensional Stability
| | | | | 用途 | | | 機構評級 | | | RoHS 合規性 | | | 形式 | | | 加工方法 | | | 多點數據 | - Creep Modulus vs. Time (ISO 11403-1)
- Isochronous Stress vs. Strain (ISO 11403-1)
| - Isothermal Stress vs. Strain (ISO 11403-1)
- Secant Modulus vs. Strain (ISO 11403-1)
| - Shear Modulus vs. Temperature (ISO 11403-1)
- Viscosity vs. Shear Rate (ISO 11403-2)
| | | 密度 / 比重 | 1.32 | -- | g/cm3 | ASTM D792, ISO 1183 | | 熔融體積流量（MVR） (275°C/5.0 kg) | 50.0 | -- | cm3/10min | ISO 1133 | | 收縮率 - 流動 (3.18 mm) | 0.30 | -- | % | | | 吸水率 | | | | | | 飽和 | 6.0 | -- | % | ASTM D570 | | 飽和, 23°C | 6.0 | -- | % | ISO 62 | | 平衡, 50% RH | 1.9 | -- | % | ASTM D570 | | 平衡, 23°C, 50% RH | 1.9 | -- | % | ISO 62 | | 拉伸模量 (23°C) | 8600 | 6500 | MPa | ISO 527-2 | | 抗張強度 | | | | | | 斷裂, 23°C | 179 | -- | MPa | ASTM D638 | | 斷裂, -40°C | 196 | 186 | MPa | ISO 527-2 | | 斷裂, 23°C | 170 | 120 | MPa | ISO 527-2 | | 伸長率 | | | | | | 斷裂, 23°C | 3.0 | -- | % | ASTM D638 | | 斷裂, -40°C | 2.9 | 2.7 | % | ISO 527-2 | | 斷裂, 23°C | 3.0 | 6.0 | % | ISO 527-2 | | 彎曲模量 | | | | | | 23°C | 7930 | -- | MPa | ASTM D790 | | 23°C | 7600 | -- | MPa | ISO 178 | | 簡支梁缺口沖擊強度 | | | | ISO 179 | | -30°C | 9.0 | -- | kJ/m2 | | | 23°C | 10 | 18 | kJ/m2 | | | 簡支梁無缺口沖擊強度 | | | | ISO 179 | | -30°C | 55 | -- | kJ/m2 | | | 23°C | 65 | 90 | kJ/m2 | | | 懸壁梁缺口沖擊強度 | | | | | | -40°C | 53 | -- | J/m | ASTM D256 | | 23°C | 96 | -- | J/m | ASTM D256 | | 23°C | 9.5 | -- | kJ/m2 | ISO 180 | | 載荷下熱變形溫度 | | | | | | 0.45 MPa, 未退火 | 250 | -- | °C | ASTM D648, ISO 75-2/B | | 1.8 MPa, 未退火 | 250 | -- | °C | ASTM D648, ISO 75-2/A | | 熔融峰值溫度 | 260 | -- | °C | ASTM D3418, ISO 3146 | | 線形熱膨脹系數 | | | | | | 流動 | 1.0E-5 | -- | cm/cm/°C | ASTM E831 | | 流動 | 3.0E-5 | -- | cm/cm/°C | | | 橫向 | 6.5E-5 | -- | cm/cm/°C | | | RTI Elec | | | | UL 746 | | 0.8 mm | 130 | -- | °C | | | 1.5 mm | 130 | -- | °C | | | 3.0 mm | 130 | -- | °C | | | RTI Imp | | | | UL 746 | | 1.5 mm | 120 | -- | °C | | | 3.0 mm | 120 | -- | °C | | | RTI | | | | UL 746 | | 1.5 mm | 130 | -- | °C | | | 3.0 mm | 130 | -- | °C | | | 體積電阻率 | | | | | | 1.50 mm | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 | | -- | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 | | 介電常數 (1 MHz) | 3.50 | 5.50 | | IEC 60250 | | 耗散因數 | | | | IEC 60250 | | 100 Hz | 0.014 | 0.30 | | | | 1 MHz | 0.014 | 0.16 | | | | 漏電起痕指數 | 550 | 550 | V | IEC 60112 | | UL 阻燃等級 | | | | UL 94 | | 0.8 mm | HB | -- | | | | 1.5 mm | HB | -- | | | | 3.0 mm | HB | -- | | | | 干燥溫度 | 80 | °C | | | 干燥時間 | 2.0 到 4.0 | hr | | | 建議的最大水分含量 | 0.15 | % | | | 加工（熔體）溫度 | 280 到 305 | °C | | | 模具溫度 | 80 到 90 | °C | | | 注塑壓力 | 3.50 到 12.5 | MPa | | | 注射速度 | 快速 | | | 深圳市贏順塑膠原料有限公司，專業銷售各種食品級尼龍，加纖尼龍，防火尼龍，導電尼龍，電子絕緣尼龍，耐高溫尼龍，耐寒尼龍，耐油尼龍，耐候抗UV尼龍,電話：18818688291 歡迎新老客戶來電咨詢合作！ |